STRESSPROOF STEEL 1144 是什么材料？

lee1211 · 发表于 2008-10-5 18:20:41

提示: 作者被禁止或删除内容自动屏蔽

cuteyppy · 发表于 2008-10-5 20:28:06

STRESSPROOF® is made by a patented process which consists of drawing the bar through a special die under heavy draft, then stress relieving it. This severe cold working combined with the stress relieving results in a high strength bar with good stability and exceptional machinability. STRESSPROOF® can often replace heat treated alloy steel for machined parts requiring hardness in the range 23-30 HRC. It can be induction hardened but should be watched for quench cracks because of the high sulfur and manganese content. Welding is not recommended. STRESSPROOF® exceeds ASTM A311, Class B.
看看上面的信息对您是否有帮助，好像比较特别的材料

hanjixian · 发表于 2008-10-5 20:57:22

1144是美国牌号，为含硫易切削碳素钢，其成分为C：0.4-0.48%；Mn：1.35-1.65；P≤0.04%；S：0.24-0.33%

[ 本帖最后由 hanjixian 于 2008-10-5 21:01 编辑 ]

lcshjsb · 发表于 2008-10-5 21:09:31

是易切削钢，硬度HRC36不算低，但必须经调质处理！！！

lee1211 · 发表于 2008-10-5 23:23:59

提示: 作者被禁止或删除内容自动屏蔽

panwenzhang0515 · 发表于 2008-10-10 16:03:01

易切削钢,S比较高.
C% Mn% P% S%
0.40-0.48 1.35-1.65 0.040max 0.24-0.33

		自动登录	找回密码
密码			注册

通知

[求助] STRESSPROOF STEEL 1144 是什么材料？

评分

浏览过的版块

lee1211 lee1211 当前离线积分 286 UID 10587 主题在线时间小时注册时间 2006-1-25 头像被屏蔽	发表于 2008-10-5 18:20:41 \| 显示全部楼层 \|阅读模式来自：中国提示: 作者被禁止或删除内容自动屏蔽

	回复举报

lee1211 lee1211 当前离线积分 286 UID 10587 主题在线时间小时注册时间 2006-1-25 头像被屏蔽	楼主\| 发表于 2008-10-5 23:23:59 \| 显示全部楼层来自：中国提示: 作者被禁止或删除内容自动屏蔽

	回复支持反对举报