1.4529是什么钢材啊,焊接怎样.

hrzhrz

1.4529是什么钢材啊,焊接怎样.

guos

1.4529 是6Mo不锈钢合金
( n4 y- C" m/ n1 Z" W8 k/ | C       Mn     Si       P      S          Ni                 Cr            Mo            N
0.02   1.0  0.5   0.03    0.01   24.0~26.0  19.0~21.0   6.0~7.0   0.15~0.25 Cu 0.5~1.5
/ Y! B: @  t. q8 p+ L/ A9 t1 K" y
- R: D3 a) k) L$ Z2 U% C焊接只能采用氩弧焊

yangnj

1.4529是德国标准，相当于904L，可以使用焊条焊接！具体的焊条牌号，我得查下了！

meiguihai

1.4529德国表示钢铁材料的一种方法
* ~4 v6 z6 [3 z( p9 M德国牌号：X1NiCrMoCuN25-20-7

ZEDIO

Material number 1.4529     -     X1NiCrMoCuN25-20-7

3 ~5 j! t+ k5 T' h4 }% b
Composition in % :
' @& f3 E3 Y( ?9 e3 v
C max. 0,02
Si max. 1,00
5 K- F% u# K" W; l; |3 g% J( CMn max. 2,00
" w5 @% R% W; xP max. 0,030
; L( m4 v1 M3 e' @- c1 {S max. 0,015
Cr 19,00 - 21,00
" i6 p" q6 ^# U0 |% wMo 6,00 - 7,00
$ x8 _- h. u6 P( A" r5 q/ ONi 24,00 - 26,00
2 R3 |: s$ ?# z% x7 i" BCu 0,50 - 1,50
* q! B7 D; v9 h# x  d1 D& w6 CN 0,10 - 0,25
8 c( r+ \, @" O6 o1 C; K, f; B/ hRange of application and heat treatment :
/ R. Q; {; G# G) F4 K
! b# b; d2 v( \  LStainless steel : sea technology , heat exchanger at strong strains
2 X8 l7 G9 I0 @! ?2 tSolution annealing : 1120 - 1180 °C (air or water)
5 `" P( N/ Z; x  D
[ 本帖最后由 ZEDIO 于 2008-1-24 21:49 编辑 ]

willing2002

看看这个                                

miracleer

Designation:    X1NiCrMoCuN25-20-7  

Material Number:    1.4529  

  Y$ v1 p  o& @" {/ |' f Material Type:    Stainless steel, austenitic, Steel for pressure vessels  
! R2 G/ d: {3 F  J* |' a4 @& ^
+ {! X* F1 q0 u Organisation:    CEN, European Committee for Standardization  

Region:    Europe
& ~' J$ m6 {, \! r7 Q. v# oEN 10088-1-2-3, EN 10028-7, EN 10250-4, EN 10222-1-5

7 t# [1 `9 r3 v% ahardness Rockwell B max.:      

! G/ h7 \! w  x% z3 q hardness Rockwell C max.:      

7 Q) b3 H% ^. ]1 |  s+ n) P
. I" q% L3 L" U" i1 U" h' l. U hardness Vickers max.:      
( U6 V" ]/ E6 D
0 p# w5 J: f7 \ hardness Brinell max.:      

0 `4 O; d6 E7 Z/ f1 `7 N; r" d
yield strength min. [MPa]:    300  
# n# b0 w4 d' f6 g
# A$ R" I8 e5 |3 Y yield strength max. [MPa]:      
6 f; K; T5 W1 K3 m; N

1% - yield strength min. [MPa]:    340  

  Q: X7 h6 a0 I* `% f8 N6 S
tensile strength min. [MPa]:    650  
! f- i3 `8 z4 V
tensile strength max. [MPa]:    850  


: b. F3 X& r; L9 O# `$ O( X elongation to fracture longitudinal min. [%]:    40  

elongation to fracture transverse min. [%]:      
! b; p7 B2 T) @: k2 Q) m
8 L: _5 z" d6 ^. s reduction of area min. [%]:      

# d$ u8 e7 N2 |4 x" D4 o
, q7 B5 B. v  D" k charpy v notch toughness transverse min. [J]:    60  
* [- x9 y- `: k3 o) V
charpy v notch toughness longitudinal min. [J]:    90

lyp660201

我厂刚采用此板进行了爆炸焊接，厚度规格为3+8，需要缺陷修补，也需咨询焊接问题

laoli8341

可以用ENISO 14172:2006: E Ni 6625 (NiCr22Mo9Nb)
0 U" ^) l; p5 d+ k+ A5 w2 y0 Q" HAWS A5.11-05: ENiCrMo-3焊条焊接

cylin123