请问抛光 POLISH S.P.I C3所对应的粗糙度是多少？

fath

客户要求Polish S.P.I C3，不过我们生产单位无对应标准
请教大家
% X& `- c3 U1 S8 C* Q% T
. C5 a9 t$ O% E; r6 t+ O/ n' X抛光 Polish S.P.I 标准的C3所对应的粗糙度是多少？

xhq004

等同于320号油石抛光效果，具体粗糙度不大清楚。

mideas

An SPI A-1 Diamond Finish is a specialty of Bales Mold Service. We use it to produce the finest finish on molds, producing highly visible or lens quality parts. The SPI A-2 is the most widely used diamond finish, providing good release and good visual parts. An SPI A-3 is a fine choice for release where a high gloss appearance is not required. All diamond finishes work well with chrome and nickel.
0 q- D, U2 R& e6 ?8 U7 f
# Y( h  w% \/ p- s0 g

" ]; W+ A2 P. z5 z; KBales also offers:
. D4 e8 e6 |) l! n0 k+ L0 ePaper Finishes, SPI B-1 to B-3 – Next to diamond polishing, paper finishes are the second most refined finishes available. Paper finishes produce a slightly reflective or glossy shine and very good release. They are often recommended for products that do not require a big decorative or visual impact.  
; C6 U3 o4 ]) F. w2 j+ p3 |: U8 TStone Finishes, SPI C-1 to C-3 – The most economical finish, stone finishes are also the first step in the process of creating both the paper and diamond finishes. Stone finishes provide good release but very little gloss to the plastic part. This is a good choice for strictly functional molded parts where aesthetics are of no importance.
# l; {! t% |  T5 R8 S( f: n: `" EBlast Finishes, SPI D-1 to D-3 – When done properly, blasted finishes can produce some of the most interesting stipples and textures on mold surfaces. From a fine satin texture with varied degrees of gloss to a flat, no-gloss coarse stipple, Bales has the blast media to produce the proper finish for you. Blast finishes are also an excellent way to camouflage weld repairs and slight imperfections

mideas

就是表面光洁度的美国一个标准，如果是钢料的话我就是知道用320号的油石经过加工得到的效果，平均Ra u-in 38-42 SPI-C1 (600 Stone)
SPI-B1 (600 Paper)
0 U. j# Q% E- TSPI-A2(High polish)

( W. U4 z9 o; B5 T[ 本帖最后由 mideas 于 2008-5-19 15:43 编辑 ]

mideas

NOMENCLATURE


4 D4 {5 b# U+ _4 }SPI Finish A-1 -- Grade #3, 6000 Grit Diamond Buff
! j$ q: p8 _" O
SPI Finish A-2 -- Grade #6, 3000 Grit Diamond Buff
) M0 c, J) r* i4 w. ?( Y; z( _1 ^
$ S# ^  ?6 x: V( w/ HSPI Finish A-3 -- Grade #15, 1200 Grit Diamond Buff
' F, r/ q5 H5 r% s) x3 K: o
SPI Finish B-1 -- 600 Grit Paper

SPI Finish B-2 -- 400 Grit Paper

SPI Finish B-3 -- 320 Grit Paper
# e7 W8 I1 J3 E7 T# P
2 s% j' u6 d, nSPI Finish C-1 -- 600 Grit Stone

& |" W" @/ y$ m& GSPI Finish C-2 -- 400 Grit Stone
: [, X0 y4 q$ u& O+ V5 z
; d' g2 K5 ^  y4 a9 p0 WSPI Finish C-3 -- 320 Grit Stone
5 Y, ~& v, C: i9 H2 k4 Q  n. E
! W/ a$ B/ |, ^2 Y  f2 D4 HSPI Finish D-1 -- 600 Stone Prior to Dry Blast Glass Bead #11

' W( u8 s8 ~6 k% D1 {5 z! ^SPI Finish D-2 -- 400 Stone Prior to Dry Blast #240 Oxide
+ V5 Y5 L9 h1 v: H& m& ?& w# {
0 s. Q) D, |( H2 ~% gSPI Finish D-3 -- 320 Stone Prior to Dry Blast #24 Oxide                    

( ~* `- i2 k" T( U+ ~" y- U) N/ G; aSPE -- The Society of Plastic Engineers

SPI -- The Society of the Plastic Industry
0 F6 ?2 v- B8 [  u6 t* M1 [
[ 本帖最后由 mideas 于 2008-5-19 15:46 编辑 ]

fath

多谢各位达人的帮忙,问题已经解决 :victory: :victory:
0 I1 d( x6 B" ?4 }4 L" b
' T7 |+ P4 U5 C9 u; G8 n7 l么么

anny.li

各位大虾：
    我有看过有这样的资料，请问我应该以那一份资料为主。其中有1000#。2000#号沙纸纹是什么意思，用400#的沙纸咋会有2000#的沙纸纹？


# V+ x& n  t$ {9 {/ T+ y0 Q另附：表面粗糙度国际标准加工方法
标准等级代号 表面粗糙度 加工工具(方法) 加工材料及硬度要求 光度描述
- c5 U& s$ j4 M. v  g! ?/ E' f: a粗研磨砂粒粒度 精研磨砂粒粒度 钻石膏抛光
SPI(A1) Ra0.005       S136 54HRC 光洁度非常高,镜面效果

  _- S( ~' \& R/ e) `7 n) r# aSPI(A2) Ra0.01       DF-2 58HRC 光洁度较低,没有砂纸纹

- H; i7 b' V- q9 G1 s- R8 ISPI(A3) Ra0.02       S136 300HB 光洁度更低一级,但没有砂纸纹
! B1 K$ u8 d: E7 z- A" D6 k# c
+ a0 p$ Q8 u& o5 C( s# C& uSPI(B1) Ra0.05           没有光亮度,有轻微3000#砂纸纹
   
  A) `0 V7 f$ N. \  ?- ~. PSPI(B2) Ra0.1           没有光亮度,有轻微2000#砂纸纹
   
  P7 ^# r& l. A+ o% s  MSPI(B3) Ra0.2         没有光亮度,有轻微1000#砂纸纹
                   不辨加工痕迹的方向
/ ]# Y6 N2 |; \   

3 {% `" b$ l' b5 x. X( {% k  Ra0.4 精加工：精车＼精刨＼精铣＼磨＼铰＼刮  
   
  微辨加工痕迹的方向
  Ra0.8 精加工：精车＼精刨＼精铣＼磨＼铰＼刮     可辨加工痕迹的方向
  Ra1.6         
% O, G/ Z9 i4 L& ?8 f  Ra3.2         
  Ra6.3         
/ a2 c; `$ V& \3 Q4 T  o/ t  Ra12.5         
0 Z5 a; k$ m2 l% ~  `" C! j9 y  Ra25         
( w( _' i/ F1 V, I  Ra50         
7 @9 x) y/ ?3 v: O3 P  h
:(

wuaimin

好资料，找了很久，谢了。