顶楼：What's the meaning of "copper flash finish"? Please kindly help me translate the surface treatment of the gears, "copper flash finish".
Thank you in advance.

二楼：根据字面的理解应该是表面镀铜；I think

再提供一点讯息：Our products are supplied in various finished like Bluing,Blackening, Zinc, Copper, Nickel, Chromes & Cadmium Plating, as perthe requirements of our customers.

For protection againstcorrosion, zinc plated finish is available as a standard extra.Passivation is a surface treatment which further improves the corrosionresistance of the plated film but because of its yellow irridescentfinish may not be suitable for some decorative applications. For decorative effect a copper flash finish may be applied

是铜的溅射喷镀（表面）处理

三楼： 闪镀 flash(flash plate) 电时间极短产生薄层的电镀。
按上述，可否理解为闪镀铜

。。。。。。

j.chen404 · 发表于 2010-1-26 13:28:46

主要目的是在不需渗碳处理的部位沉积一薄层铜，防止后期淬火时将不需要的部位淬硬了

csdlfj001 · 发表于 2010-1-26 15:40:59

闪镀铜：在经预处理的工件表面上形成一层较薄的铜层，而此过程仅需30~90s，习惯上称为闪铜。

nel1982 · 发表于 2010-1-27 15:09:41

同意一楼的说法，表面镀铜是为防止渗碳，为将来的淬火处理进行涂层防护。二楼所说的闪镀铜国内改进之后的工艺无需闪铜，直接镀金属粉即可！

wingman · 发表于 2010-1-29 08:04:09

本帖最后由 wingman 于 2010-1-30 09:49 编辑

同意一楼的说法，表面镀铜是为防止渗碳，为将来的淬火处理进行涂层防护。二楼所说的闪镀铜国内改进之后的工艺无需闪铜，直接镀金属粉即可！6 h& [4 R) e w' _
nel1982 发表于 2010-1-27 15:09 http://www.3dportal.cn/discuz/images/common/back.gif

原来是这样。

nel1982 · 发表于 2010-1-29 16:05:07

楼上的原来工艺已经更改了什么意思呢？难道不是“闪镀铜”？

wingman · 发表于 2010-1-30 09:50:45

楼上的原来工艺已经更改了什么意思呢？难道不是“闪镀铜”？
1 r! W" X6 t3 g8 b1 o, znel1982 发表于 2010-1-29 16:05 http://www.3dportal.cn/discuz/images/common/back.gif

不好意思是我写的时候没考虑好。让你误解了。

zamcompy · 发表于 2010-1-30 12:00:09

应当是化学镀铜

trues2006 · 发表于 2010-1-31 22:11:11

闪镀，一种通电时间极短，只产生很薄的镀层的电镀工艺，英语通常翻译为，flash painting;
可以理解为闪镀铜，即是以铜作为电镀介质进行电镀；