什么铜材能达到下面的要求？？

niat010113

我们有个客户需要能满足下面性能的铜材！请大家指导下
e-module:135*10^3Nmm^2
yield strength:490Nmm^2
tensile strength:580-680Nmm^2
' Z1 u1 P0 D# r/ A5 ]2 @) d5 q. L请专家组提供意见

lzxh

铍铜（QBe）通过控制淬火时效工艺参数可达到上述指标。

hourpp

材料： CuNi 18 Zn 20 标准： DIN 国家与地区： Germany 金属类别： Copper Alloy 次级类别： DIN 17663 Wrought alloys ( d! d7 `/ Q0 i1 ]2 |$ \0 R6 D

http://www.key-to-nonferrous.com/cn/img/nav/content-bgf.gif

http://www.key-to-nonferrous.com/cn/img/nav/spacer.gif

http://www.key-to-nonferrous.com/cn/img/nav/spacer.gif

化学成分 (%) , D& h  H) V3 m  J http://www.key-to-nonferrous.com/cn/img/nav/spacer.gif 2 ]! @. o* f! x. X' t 元素 最小 最大 近似的 Cu 60.0000 63.0000 Mn 0.7000 " J5 }; t% R5 E. n" ~* h' e8 ? Zn (*) 2 r! f9 u6 K* B8 w ) j/ Z+ e% A0 D8 g" `; o! y( M Ni 17.0000 19.0000 ! R' v( K$ i5 o! b. G% O Pb % v5 ?8 a; q( X/ @5 C 0.0300 0 D. h* t- t, ~/ A Sn / y" a* {6 ~7 C 0.2000 Fe % r# ~0 \4 G4 o/ z 0.3000 % G3 @" _4 d$ x Tot. other 0.1000 7 X, E1 X; m1 Q( o/ v http://www.key-to-nonferrous.com/cn/img/nav/spacer.gif ! G. h) Y8 a7 _$ Y) G 元素 注释 Zn Remainder 3 @' A' \. r5 D/ F$ ]; G

材料属性 7 \5 u* _$ R9 _e-module:135kN/mm^2

http://www.key-to-nonferrous.com/cn/img/nav/spacer.gif
  d+ A' d# U* i2 x

	Min.	Max.	Approx.
F 38 ; Plate, DIN 17670 ; 0.2-5 mm
Yield Stress, Rp0,2 (MPa):	290
Tensile Stress, Rm (MPa):	370	430
Elongation, A (%):	40
Comment:	Elongation Lo=5 mm
Hardness:	90 HB
F 38 ; Strip, DIN 17670 ; 0.2-5 mm
Yield Stress, Rp0,2 (MPa):	290
Tensile Stress, Rm (MPa):	370	430
Elongation, A (%):	40
Comment:	Elongation Lo=5 mm
Hardness:	90 HB
F 38 ; Tube, DIN 17671 ; <3 mm
Yield Stress, Rp0,2 (MPa):		290
Tensile Stress, Rm (MPa):	370	440
Elongation, A (%):	40
Comment:	Elongation Lo=5 mm
Hardness:	95 HB
F 44 ; Plate, DIN 17670 ; 0.2-5 mm
Yield Stress, Rp0,2 (MPa):	290
Tensile Stress, Rm (MPa):	430	520
Elongation, A (%):	22
Comment:	Elongation Lo=5 mm
Hardness:	130 HB
F 44 ; Strip, DIN 17670 ; 0.2-5 mm
Yield Stress, Rp0,2 (MPa):	290
Tensile Stress, Rm (MPa):	430	520
Elongation, A (%):	22
Comment:	Elongation Lo=5 mm
Hardness:	130 HB
F 53 ; Plate, DIN 17670 ; 0.2-2 mm
Yield Stress, Rp0,2 (MPa):	440
Tensile Stress, Rm (MPa):	520	610
Elongation, A (%):	6
Comment:	Elongation Lo=5 mm
Hardness:	155 HB
F 53 ; Strip, DIN 17670 ; 0.2-2 mm
Yield Stress, Rp0,2 (MPa):	440
Tensile Stress, Rm (MPa):	520	610
Elongation, A (%):	6
Comment:	Elongation Lo=5 mm
Hardness:	155 HB
F 62 ; Plate, DIN 17670 ; 0.2-2 mm
Yield Stress, Rp0,2 (MPa):	540
Tensile Stress, Rm (MPa):	610
Elongation, A (%):	1
Comment:	Elongation Lo=10 mm
Hardness:	185 HB
F 62 ; Strip, DIN 17670 ; 0.2-2 mm
Yield Stress, Rp0,2 (MPa):	540
Tensile Stress, Rm (MPa):	610
Elongation, A (%):	1
Comment:	Elongation Lo=10 mm
Hardness:	185 HB
F 45 ; Tube, DIN 17671 ; <3 mm
Yield Stress, Rp0,2 (MPa):	290
Tensile Stress, Rm (MPa):	440	540
Elongation, A (%):	20
Comment:	Elongation Lo=5 mm
Hardness:	135 HB
F 55 ; Tube, DIN 17671 ; <2 mm
Yield Stress, Rp0,2 (MPa):	470
Tensile Stress, Rm (MPa):	540
Elongation, A (%):	6
Comment:	Elongation Lo=5 mm
Hardness:	160 HB
F 55 ; Rod, bars, DIN 17672 ; round 2-10 mm, polygonal 2-8 mm
Yield Stress, Rp0,2 (MPa):	440
Tensile Stress, Rm (MPa):	540	640
Elongation, A (%):	5
Comment:	Elongation Lo=5 mm
Hardness:	165 HB
F 40 ; Rod, bars, DIN 17672 ; round >=10 mm, polygonal >=8 mm
Yield Stress, Rp0,2 (MPa):		290
Tensile Stress, Rm (MPa):	390	470
Elongation, A (%):	40
Comment:	Elongation Lo=5 mm
Hardness:	95 HB
F 48 ; Rod, bars, DIN 17672 ; round 3-40 mm, polygonal 3-30 mm
Yield Stress, Rp0,2 (MPa):	340
Tensile Stress, Rm (MPa):	470	540
Elongation, A (%):	22
Comment:	Elongation Lo=5 mm
Hardness:	135 HB
F 65 ; Rod, bars, DIN 17672 ; round 1-4 mm
Yield Stress, Rp0,2 (MPa):	570
Tensile Stress, Rm (MPa):	640
Elongation, A (%):	1
Comment:	Elongation Lo=10 mm
Hardness:	190 HB

" C0 N) V3 W5 T: K5 j
! b- R: `7 H- g: h) ~0 h[ 本帖最后由 hourpp 于 2007-12-14 13:17 编辑 ]

niat010113

请问楼上的F40是代表什么意思，我的客户要求的是F58请解释下 谢谢

hourpp

原帖由 niat010113 于 2007-12-14 13:41 发表 http://www.3dportal.cn/discuz/images/common/back.gif
请问楼上的F40是代表什么意思，我的客户要求的是F58请解释下 谢谢

5 v. _7 c$ z3 |/ _  a

F 58 ; Wire, DIN 17677 ; 0.3-0.8 mm
Tensile Stress, Rm (MPa):	620	730
Elongation, A (%):	1
Comment:	Elongation L0=100 mm.
F 58 ; Wire, DIN 17677 ; 0.8-1.5 mm
Tensile Stress, Rm (MPa):	610	710
Elongation, A (%):	2
Comment:	Elongation L0=100 mm.
F 58 ; Wire, DIN 17677 ; 1.5-3 mm
Tensile Stress, Rm (MPa):	600	690
Elongation, A (%):	3
Comment:	Elongation L0=100 mm.
F 58 ; Wire, DIN 17677 ; 3-8 mm
Tensile Stress, Rm (MPa):	580	660
Elongation, A (%):	3
Comment:	Elongation L0=100 mm.

$ l) w' Q* T$ R" m8 g
F代表什么我也不知道，可能是第多少条款。

niat010113

多少是看明白了一点，不知道楼上的兄弟那里找的资料啊 ？？